#SH350 DAFLEX Heat Shrinkable Irradiated Kynar® Tubing AMS-DTL-23053/8
|
|
Product Options
| Catalog Number: |
|
|
Description: DAFLEX KYNAR, a semi-rigid shrinkable polyvinylidene (PVDF) fluoride tubing, is free from flaws, pin holes, seams, cracks or inclusions. It is a tough, high temperature, thin wall tubing with high cut through and abrasion resistance. It shrinks 50% in diameter and 10% longitudinally when heated to approximately 347°F/175°C.
DAFLEX Shrinkable KYNAR tubing will not cold flow, melt or split when shrunk over irregularly shaped objects. Conforms to Mil-I-23053/8 and AMS-DTL-23053/8.
This series is RoHS compliant.
| DAFLEX Heat Shrinkable Irradiated Kynar Tubing |
|---|
DABURN
Cat. No. | I.D. As Supplied | Recovered (After Heating) | Feet/Standard Package* | M23053/8 |
|---|
| I.D. Max. | Nom. Wall Thickness |
|---|
| Size | IN. | MM. | IN. | MM. | IN. | MM. | 4' Lengths | 6" Lengths#* |
|---|
| SH350-3/64 |
3/64 |
0.046 |
1.170 |
0.023 |
0.580 |
0.010 |
0.250 |
100' |
16 |
-001 |
| SH350-1/16 |
1/16 |
0.063 |
1.600 |
0.031 |
0.790 |
0.010 |
0.250 |
100' |
14 |
-002 |
| SH350-3/32 |
3/32 |
0.093 |
2.360 |
0.046 |
1.170 |
0.010 |
0.250 |
100' |
12 |
-003 |
| SH350-1/8 |
1/8 |
0.125 |
3.180 |
0.062 |
1.570 |
0.010 |
0.250 |
100' |
10 |
-004 |
| SH350-3/16 |
3/16 |
0.187 |
4.750 |
0.093 |
2.360 |
0.010 |
0.250 |
100' |
8 |
-005 |
| SH350-1/4 |
1/4 |
0.250 |
6.350 |
0.125 |
3.180 |
0.012 |
0.300 |
100' |
6 |
-006 |
| SH350-3/8 |
3/8 |
0.375 |
9.530 |
0.187 |
4.750 |
0.012 |
0.300 |
100' |
4 |
-007 |
| SH350-1/2 |
1/2 |
0.500 |
12.700 |
0.250 |
6.350 |
0.012 |
0.300 |
20'* |
2 |
-008 |
| SH350-3/4 |
3/4 |
0.750 |
19.050 |
0.375 |
9.530 |
0.017 |
0.430 |
20'* |
1 |
-009 |
| SH350-1" |
1" |
1.000 |
25.400 |
0.500 |
12.700 |
0.019 |
0.480 |
20'* |
.5 |
-010 |
® Pennsalt Chemical Co.
# Order as SH350PA-3/64 i.e., please call For pricing and to order
* Please call to order quantities less than 100'.
|
Operating Temperature:
|
-55°C to +175°C. |
|---|
|
Stock Color:
|
Clear |
|---|
|
Product Reviews
|
|